Shangflon®FL2606 - Extrusion Grade PVDF | Copolymer, Suitable For Extruding Pipes, Bars And Plates PVDF

Shangflon®FL2606 - Extrusion Grade PVDF | Copolymer, Suitable For Extruding Pipes, Bars And Plates PVDF
Shangflon®FL2606 - Extrusion Grade PVDF | Copolymer, Suitable For Extruding Pipes, Bars And Plates PVDF

Shangflon®FL2606 - Extrusion Grade PVDF | Copolymer, Suitable For Extruding Pipes, Bars And Plates PVDF

Low to medium viscosity grade with low permeability to most gases and liquids for easy melt processing by standard extrusion.
Categories PVDF Extrusion Grade
Brand Shangflon PVDF & Flurine FKM Manufacturer
Model FL2606
Features Copolymer, Medium and low viscosity
Uses Extruded pipe, Bar, Plate
Forms Translucent white particles
Update Time Nov 11,2023
Detail Information
Description
Description
Shangflon®FL2606 PVDF copolymer is medium and low viscosity grade that with high purity. 

Important properties include excellent chemical resistance to most aggressive substances and solvents, excellent mechanical strength and toughness, high abrasion resistance, high temperature capabilities, excellent aging resistance, low permeability to most gases and liquids and easily melt-processed by standard methods of extrusion.
Technical Specifications
General
Features Copolymer, Medium and low viscosity
Uses Extruded pipe, Bar, Plate
Forms Translucent white particles
Items Typical Value FL2606 Test Method
Physical Properties
Density(g/cc) 1.77~1.80 ASTM D792
Melt Flow Rate(g/10min) 4.0~8.0 Load 5kg, 230℃,ASTM D1238
Melt viscosity(Kps) 10~15 Shear Rate 100 1/s, ASTM D3835
Water Absorption(%)(Time 24 hr) ≤0.040 ISO 62
Linear Mold Shrinkage(cm/cm) 0.0200~0.0300
Molecular Properties
Molecular weight(Da) 350,000~440,000 GPC,DMF,ISO 16014
Intrinsic viscosity(dl/g) 1.10~1.30 30℃,DMAC
Molecular weight distribution 2.0-3.0 GPC,DMF,ISO 16014
Mechanical Properties
Tensile Modulus(Thickness2.00mm)(MPa) 800~1200 1.0mm/min,ASTM D638
Flexural Modulus(Thickness2.00mm)(MPa) 700~1000 2.0mm/min,ASTM D790
Yield Strength(Thickness2.00mm)(MPa) 30.0~40.0 50mm/min,ASTM D638
Break Strength(Thickness2.00mm)(MPa) 20.0~35.0 50mm/min,ASTM D638
Elongation at Yield(%) 10.0~15 50mm/min,ASTM D638
Elongation at Break(%) 200~600 50mm/min,ASTM D638
Hardness, Shore D(Thickness2.00mm) 70~75 ASTM D2240
Izod Impact, Notched(Thickness 4.00mm, 23℃)(J/m) 150~200 Notched V 10 mm
ASTM D256
Thermal Properties
Melting Point(℃) 158~166 ASTM D3418
Crystallization Temperature(DSC peak)(℃) 115~130 ASTM D3418
Glass Transition Temp, Tg(℃) -32.0 ASTM E1356
Decomposition Temperature(℃) 330~350 1% wt. loss / in air
Vicat Softening Point(℃) 90~105 ASTM D1525
Heat deflection temperature at 1.8 MPa(Thickness 4.00mm)(℃) 50~60 After annealing 150℃,16h
ASTM D648
Electrical Properties
Surface Resistance(ohm) ≥1.00E+14 VoltageASTM D257
Electrical Resistivity(ohm·cm) ≥1.00E+14 Intensity=10mA,After 2 min@23℃
ASTM D257
Dielectric strength(Thickness 1.00mm,23℃)(KV/mm) 20~25 ASTM D149
Dielectric constant(1kHz,23℃) 7.0~10.0 ASTM D150
Burning Properties
UL Flame retardant grade(0.100mm) V-0 UL94
Oxygen Index(3.00mm) 44% ASTM D2683
Process safety instructions
1)This product should be processed under 260℃ to avoid producing toxic gases.
2)PVDF has good fire resistance and smoke inhibition property. While, it will release toxic hydrogen fluoride gas and fluorocarbon compounds when meets with fire.
3)Operators should pay attention to personal protection during the processing and operating.
Packaging and storage
PVDF is packed in a plastic bag and then be put into a PE bag with the net weight 25KGS. It must be stored in clean, cool, dry place.

Contact Immediately

We have a dedicated team of technical experts ready to assist you with your most challenging projects. Discover cost-effective customized solutions for exceptional performance and value. Contact us today – we are eager to take on the challenge!
*Email
Name
Tel
*Title
*Content

Let's Innovate Together

We have a dedicated team of technical experts ready to help you with your most challenging projects, so contact us today - we're ready for the challenge!
is a tech enterprise specializing in fluorine-based materials. We drive renewable energy and sustainability through innovation.